{glossarbot=disable}Melting point

1 H hydrogen (H2)
use	14.01 K	-259.14 °C	-434.45 °F
WEL	14.01 K	-259.14 °C	-434.45 °F
CRC		-259.34 °C
LNG		-259.35 °C
2 He helium
use	0.95 K (at 2.5 MPa)	-272.2 °C (at 2.5 MPa)	-458 °F (at 2.5 MPa)
WEL	0.95 K	-272.2 °C	-458 °F
LNG		-272.15 °C (at 25 atm)
3 Li lithium
use	453.69 K	180.54 °C	356.97 °F
WEL	453.69 K	180.54 °C	356.97 °F
CRC		180.50 °C
LNG		180.54 °CC
beryllium
usese	1560 K	1287 °C	2349 °F
WEL	1560 K	1287 °C	2349 °F
CRC		1287 °C
LNG		1287 °C
5 B boron
use	2349 K	2076 °C	3769 °F
WEL	2349 K	2076 °C	3769 °F
CRC		2075 °C
LNG		2076 °C
6 C carbon (graphite)
use
WEL	? (3800 K)	? (3527 °C)	? (6381 °F)
CRC		tp 4489 °C (at 10.3 MPa)
LNG		subl. (3915–4020) °C
6 C carbon (diamond)
use
WEL	? (3800 K)	? (3527 °C)	? (6381 °F)
CRC		4440 °C (at 12.4 GPa)
LNG		(at 63.5 atm) 3500 °C
7 N nitrogen (N2)
use	63.15 K	-210.00 °C	-346.00 °F
WEL	63.05 K	-210.1 °C	-346.18 °F
CRC		-210.00 °C
LNG		-210.01 °C
8 O oxygen (O2)
use	54.36 K	-218.79 °C	-361.82 °F
WEL	54.8 K	-218.3 °C	-360.9 °F
CRC		-218.79 °C
LNG		-218.4 °C
9 F fluorine (F2)
use	53.53 K	-219.62 °C	-363.32 °F
WEL	53.53 K	-219.62 °C	-363.32 °F
CRC		tp -219.67 °C
LNG		-219.61 °C
10 Ne neon
use	24.56 K	-248.59 °C	-415.46 °F
WEL	24.56 K	-248.59 °C	-415.46 °F
CRC		-248.59 °C
LNG		-248.67 °C
11 Na sodium
use	370.87 K	97.72 °C	207.9 °F
WEL	370.87 K	97.72 °C	207.9 °F
CRC		97.80 °C
LNG		97.82 °C
12 Mg magnesium
use	923 K	650 °C	1202 °F
WEL	923 K	650 °C	1202 °F
CRC		650 °C
LNG		651 °C
13 Al aluminium
use	933.47 K	660.32 °C	1220.58 °F
WEL	933.47 K	660.32 °C	1220.58 °F
CRC		660.32 °C
LNG		660.323 °C
freezing point 933.473 K (660.323 °C) fixed point on ITS-90
14 Si silicon
use	1687 K	1414 °C	2577 °F
WEL	1687 K	1414 °C	2577 °F
CRC		1414 °C
LNG		1412 °C
15 P phosphorus (white)
use	317.30 K	44.15 °C	111.47 °F
WEL	317.3 K	44.2 °C	111.6 °F
CRC		44.15 °C
LNG		44.15 °C
15 P phosphorus (red)
use	870 K	597 °C	1107 °F
CRC		tp 590 °C
LNG		597 °C
15 P phosphorus (black)
use	883 K	610 °C	1130 °F
CRC		610 °C
LNG
16 S sulfur (orthorhombic, alpha)
use	(trans. to beta) 368.4 K	(trans. to beta) 95.3 °C	(trans. to beta) 203.5 °F
CRC		(trans. to mono) 95.3 °C
LNG		(trans. to beta) 94.5 °C
16 S sulfur (monoclinic, beta, trans. slowly to alpha)
use	388.36 K	115.21 °C	239.38 °F
WEL	388.36 K	115.21 °C	239.38 °F
CRC		119.6 °C
LNG		115.21 °C
16 S sulfur (gamma)
use	380.0 K	106.8 °C	224.2 °F
LNG		106.8 °C
17 Cl chlorine (Cl2)
use	171.6 K	-101.5 °C	-150.7 °F
WEL	171.6 K	-101.5 °C	-150.7 °F
CRC		-101.5 °C
LNG		-101.5 °C
18 Ar argon
use	83.80 K	-189.35 °C	-308.83 °F
WEL	83.8 K	-189.3 °C	-308.7 °F
CRC		-189.35 °C
LNG		-189.38 °C
19 K potassium
use	336.53 K	63.38 °C	146.08 °F
WEL	336.53 K	63.38 °C	146.08 °F
CRC		63.5 °C
CR2		63.38 °C
LNG		63.38 °C
20 Ca calcium
use	1115 K	842 °C	1548 °F
WEL	1115 K	842 °C	1548 °F
CRC		842 °C
LNG		842 °C
21 Sc scandium
use	1814 K	1541 °C	2806 °F
WEL	1814 K	1541 °C	2806 °F
CRC		1541 °C
LNG		1541 °C
22 Ti titanium (hexagonal)
use	1941 K	1668 °C	3034 °F
WEL	1941 K	1668 °C	3034 °F
CRC		1668 °C
LNG		1668 °C
23 V vanadium
use	2183 K	1910 °C	3470 °F
WEL	2183 K	1910 °C	3470 °F
CRC		1910 °C
LNG		1917 °C
24 Cr chromium
use	2180 K	1907 °C	3465 °F
WEL	2180 K	1907 °C	3465 °F
CRC		1907 °C
LNG		1907 °C
25 Mn manganese
use	1519 K	1246 °C	2275 °F
WEL	1519 K	1246 °C	2275 °F
CRC		1246 °C
LNG		(face-centered tetragonal) 1244 °C
26 Fe iron
use	1811 K	1538 °C	2800 °F
WEL	1811 K	1538 °C	2800 °F
CRC		1538 °C
LNG		1535 °C
27 Co cobalt
use	1768 K	1495 °C	2723 °F
WEL	1768 K	1495 °C	2723 °F
CRC		1495 °C
LNG		1494 °C
28 Ni nickel
use	1728 K	1455 °C	2651 °F
WEL	1728 K	1455 °C	2651 °F
CRC		1455 °C
LNG		1453 °C
29 Cu copper
use	1357.77 K	1084.62 °C	1984.32 °F
WEL	1357.77 K	1084.62 °C	1984.32 °F
CRC		1084.62 °C
LNG		1084.62 °C
freezing point 1357.77 K (1084.62 °C) fixed point on ITS-90
30 Zn zinc
use	692.68 K	419.53 °C	787.15 °F
WEL	692.68 K	419.53 °C	787.15 °F
CRC		419.53 °C
LNG		419.527 °C
freezing point 692.677 K (419.527 °C) fixed point on ITS-90
31 Ga gallium
use	302.9146 K	29.7646 °C	85.5763 °F
WEL	302.91 K	29.76 °C	85.57 °F
CRC		tp 29.771 °C
CR2		29.76 °C
LNG		29.7646 °C
melting point 302.9146 K (29.7646 °C) fixed point on ITS-90
32 Ge germanium
use	1211.40 K	938.25 °C	1720.85 °F
WEL	1211.4 K	938.3 °C	1720.9 °F
CRC		938.25 °C
LNG		937.3 °C
33 As arsenic
use	1090 K	817 °C	1503 °F
WEL	1090 K	817 °C	1503 °F
CRC		tp 817 °C (at 3.70 MPa)
CR2		817 °C
LNG		817 °C
34 Se selenium (hexagonal, gray)
use	494 K	221 °C	430 °F
WEL	494 K	221 °C	430 °F
CRC		220.5 °C
CR2		221 °C
LNG		217 °C
34 Se selenium (vitreous)
use	(trans. to gray) 453 K	(trans. to gray) 180 °C	(trans. to gray) 356 °F
CRC		(trans. to gray) 180 °C
35 Br bromine (Br2)
use	265.8 K	-7.3 °C	19 °F
WEL	265.8 K	-7.3 °C	19 °F
CRC		-7.2 °C
LNG		-7.25 °C
36 Kr krypton
use	115.79 K	-157.36 °C	-251.25 °F
WEL	115.79 K	-157.36 °C	-251.25 °F
CRC		tp -157.38 °C (at 73.2 kPa)
LNG		-157.36 °C
37 Rb rubidium
use	312.46 K	39.31 °C	102.76 °F
WEL	312.46 K	39.31 °C	102.76 °F
CRC		39.30 °C
CR2		39.31 °C
LNG		39.31 °C
38 Sr strontium
use	1050 K	777 °C	1431 °F
WEL	1050 K	777 °C	1431 °F
CRC		777 °C
LNG		757 °C
39 Y yttrium
use	1799 K	1526 °C	2779 °F
WEL	1799 K	1526 °C	2779 °F
CRC		1522 °C
CR2		1526 °C
LNG		1522 °C
40 Zr zirconium
use	2128 K	1855 °C	3371 °F
WEL	2128 K	1855 °C	3371 °F
CRC		1855 °C
LNG		1852 °C
41 Nb niobium
use	2750 K	2477 °C	4491 °F
WEL	2750 K	2477 °C	4491 °F
CRC		2477 °C
LNG		2468 °C
42 Mo molybdenum
use	2896 K	2623 °C	4753 °F
WEL	2896 K	2623 °C	4753 °F
CRC		2623 °C
LNG		2622 °C
43 Tc technetium (Tc-98 ?)
use	2430 K	2157 °C	3915 °F
WEL	2430 K	2157 °C	3915 °F
CRC		2157 °C
LNG		(Tc-98) 2157 °C
44 Ru ruthenium
use	2607 K	2334 °C	4233 °F
WEL	2607 K	2334 °C	4233 °F
CRC		2334 °C
LNG		2334 °C
45 Rh rhodium
use	2237 K	1964 °C	3567 °F
WEL	2237 K	1964 °C	3567 °F
CRC		1964 °C
LNG		1963 °C
46 Pd palladium
use	1828.05 K	1554.9 °C	2830.82 °F
WEL	1828.05 K	1554.9 °C	2830.82 °F
CRC		1554.9 °C
LNG		1555 °C
47 Ag silver
use	1234.93 K	961.78 °C	1763.2 °F
WEL	1234.93 K	961.78 °C	1763.2 °F
CRC		961.78 °C
LNG		961.78 °C
freezing point 1234.93 K (961.78 °C) fixed point on ITS-90
48 Cd cadmium
use	594.22 K	321.07 °C	609.93 °F
WEL	594.22 K	321.07 °C	609.93 °F
CRC		321.07 °C
LNG		321 °C
49 In indium
use	429.75 K	156.60 °C	313.88 °F
WEL	429.75 K	156.6 °C	313.88 °F
CRC		156.60 °C
LNG		156.60 °C
freezing point 429.7485 K (156.5985 °C) fixed point on ITS-90
50 Sn tin (white)
use	505.08 K	231.93 °C	449.47 °F
WEL	505.08 K	231.93 °C	449.47 °F
CRC		231.93 °C
LNG		231.928 °C
freezing point 505.078 K (231.928 °C) fixed point on ITS-90
51 Sb antimony
use	903.78 K	630.63 °C	1167.13 °F
WEL	903.78 K	630.63 °C	1167.13 °F
CRC		630.63 °C
LNG		630.7 °C
52 Te tellurium
use	722.66 K	449.51 °C	841.12 °F
WEL	722.66 K	449.51 °C	841.12 °F
CRC		449.51 °C
LNG		449.8 °C
53 I iodine (I2)
use	386.85 K	113.7 °C	236.66 °F
WEL	386.85 K	113.7 °C	236.66 °F
CRC		113.7 °C
LNG		113.60 °C
54 Xe xenon
use	161.4 K	-111.7 °C	-169.1 °F
WEL	161.4 K	-111.7 °C	-169.1 °F
CRC		tp -111.79 °C (at 81.6 kPa)
LNG		-111.8 °C
55 Cs caesium
use	301.59 K	28.44 °C	83.19 °F
WEL	301.59 K	28.44 °C	83.19 °F
CRC		28.5 °C
CR2		28.44 °C
LNG		28.44 °C
56 Ba barium
use	1000 K	727 °C	1341 °F
WEL	1000 K	727 °C	1341 °F
CRC		727 °C
LNG		726.9 °C
57 La lanthanum
use	1193 K	920 °C	1688 °F
WEL	1193 K	920 °C	1688 °F
CRC		918 °C
CR2		920 °C
LNG		920 °C
58 Ce cerium
use	1068 K	795 °C	1463 °F
WEL	1068 K	795 °C	1463 °F
CRC		798 °C
CR2		799 °C
LNG		795 °C
59 Pr praseodymium
use	1208 K	935 °C	1715 °F
WEL	1208 K	935 °C	1715 °F
CRC		931 °C
LNG		935 °C
60 Nd neodymium
use	1297 K	1024 °C	1875 °F
WEL	1297 K	1024 °C	1875 °F
CRC		1021 °C
CR2		1016 °C
LNG		1024 °C
61 Pm promethium (Pm-147 ?)
use	1315 K	1042 °C	1908 °F
WEL	1373 K	1100 °C	2012 °F
CRC		1042 °C
LNG		(Pm-147) 1080 °C
62 Sm samarium
use	1345 K	1072 °C	1962 °F
WEL	1345 K	1072 °C	1962 °F
CRC		1074 °C
CR2		1072 °C
LNG		1074 °C
63 Eu europium
use	1099 K	826 °C	1519 °F
WEL	1099 K	826 °C	1519 °F
CRC		822 °C
LNG		822 °C
64 Gd gadolinium
use	1585 K	1312 °C	2394 °F
WEL	1585 K	1312 °C	2394 °F
CRC		1313 °C
CR2		1314 °C
LNG		1312 °C
65 Tb terbium
use	1629 K	1356 °C	2473 °F
WEL	1629 K	1356 °C	2473 °F
CRC		1356 °C
CR2		1359 °C
LNG		1356 °C
66 Dy dysprosium
use	1680 K	1407 °C	2565 °F
WEL	1680 K	1407 °C	2565 °F
CRC		1412 °C
CR2		1411 °C
LNG		1412 °C
67 Ho holmium
use	1734 K	1461 °C	2662 °F
WEL	1734 K	1461 °C	2662 °F
CRC		1474 °C
CR2		1472 °C
LNG		1474 °C
68 Er erbium
use	1802 K	1529 °C	2784 °F
WEL	1770 K	1497 °C	2727 °F
CRC		1529 °C
LNG		1529 °C
talk	The Gmelin rare earths handbook lists 1522 °C and 1550 °C as two melting points given in the literature, the most recent reference [Handbook on the chemistry and physics of rare earths, vol.12 (1989)] is given with 1529 °C. The World Book encyclopedia from 2002 lists 1529 °C.
69 Tm thulium
use	1818 K	1545 °C	2813 °F
WEL	1818 K	1545 °C	2813 °F
CRC		1545 °C
LNG		1545 °C
70 Yb ytterbium
use	1097 K	824 °C	1515 °F
WEL	1097 K	824 °C	1515 °F
CRC		819 °C
CR2		824 °C
LNG		819 °C
71 Lu lutetium
use	1925 K	1652 °C	3006 °F
WEL	1925 K	1652 °C	3006 °F
CRC		1663 °C
LNG		1663 °C
72 Hf hafnium
use	2506 K	2233 °C	4051 °F
WEL	2506 K	2233 °C	4051 °F
CRC		2233 °C
LNG		2227 °C
73 Ta tantalum
use	3290 K	3017 °C	5463 °F
WEL	3290 K	3017 °C	5463 °F
CRC		3017 °C
LNG		2996 °C
74 W tungsten
use	3695 K	3422 °C	6192 °F
WEL	3695 K	3422 °C	6192 °F
CRC		3422 °C
LNG		3387 °C
75 Re rhenium
use	3459 K	3186 °C	5767 °F
WEL	3459 K	3186 °C	5767 °F
CRC		3186 °C
LNG		3180 °C
76 Os osmium
use	3306 K	3033 °C	5491 °F
WEL	3306 K	3033 °C	5491 °F
CRC		3033 °C
LNG		3045 °C
77 Ir iridium
use	2719 K	2446 °C	4435 °F
WEL	2739 K	2466 °C	4471 °F
CRC		2446 °C
LNG		2447 °C
78 Pt platinum
use	2041.4 K	1768.3 °C	3214.9 °F
WEL	2041.4 K	1768.3 °C	3214.9 °F
CRC		1768.4 °C
LNG		1769 °C
79 Au gold
use	1337.33 K	1064.18 °C	1947.52 °F
WEL	1337.33 K	1064.18 °C	1947.52 °F
CRC		1064.18 °C
LNG		1064.18 °C
freezing point 1337.33 K (1064.18 °C) fixed point on ITS-90
80 Hg mercury
use	234.32 K	-38.83 °C	-37.89 °F
WEL	234.32 K	-38.83 °C	-37.89 °F
CRC		tp -38.837 °C
LNG		-38.83 °C
81 Tl thallium
use	577 K	304 °C	579 °F
WEL	577 K	304 °C	579 °F
CRC		304 °C
LNG		303.5 °C
82 Pb lead
use	600.61 K	327.46 °C	621.43 °F
WEL	600.61 K	327.46 °C	621.43 °F
CRC		327.46 °C
LNG		327.43 °C
83 Bi bismuth
use	544.7 K	271.5 °C	520.7 °F
WEL	544.4 K	271.3 °C	520.3 °F
CRC		271.40 °C
LNG		271.5 °C
84 Po polonium
use	527 K	254 °C	489 °F
WEL	527 K	254 °C	489 °F
CRC		254 °C
LNG		254 °C
85 At astatine
use	575 K	302 °C	576 °F
WEL	575 K	302 °C	576 °F
CRC		302 °C
LNG		302 °C
86 Rn radon
use	202 K	-71 °C	-96 °F
WEL	202 K	-71 °C	-96 °F
CRC		-71 °C
LNG		-71 °C
87 Fr francium
use	300 K	27 °C	80 °F
CRC		27 °C
88 Ra radium
use	973 K	700 °C	1292 °F
WEL	973 K	700 °C	1292 °F
CRC		700 °C
LNG		700.1 °C
89 Ac actinium (Ac-227 ?)
use	circa 1323 K	circa 1050 °C	circa 1922 °F
WEL	1323 K	1050 °C	1922 °F
CRC		1051 °C
LNG		(Ac-227) 1050(50) °C
90 Th thorium
use	2115 K	1842 °C	3348 °F
WEL	2115 K	1842 °C	3348 °F
CRC		1750 °C
LNG		1750 °C
91 Pa protactinium
use	1841 K	1568 °C	2854 °F
WEL	1841 K	1568 °C	2854 °F
CRC		1572 °C
92 U uranium
use	1405.3 K	1132.2 °C	2070 °F
WEL	1405.3 K	1132.2 °C	2070 °F
CRC		1135 °C
LNG		1135 °C
93 Np neptunium
use	917 K	644 °C	1191 °F
WEL	910 K	637 °C	1179 °F
CRC		644 °C
LNG		644 °C
94 Pu plutonium
use	912.5 K	639.4 °C	1182.9 °F
WEL	912.5 K	639.4 °C	1182.9 °F
CRC		640 °C
LNG		639.5 °C
95 Am americium
use	1449 K	1176 °C	2149 °F
WEL	1449 K	1176 °C	2149 °F
CRC		1176 °C
LNG		1176 °C
96 Cm curium (Cm-244 ?)
use	1613 K	1340 °C	2444 °F
WEL	1613 K	1340 °C	2444 °F
CRC		1345 °C
LNG		(Cm-244) 1340 °C
97 Bk berkelium (alpha)
use	1323 K	1050 °C	1922 °F
CRC		1050 °C
LNG		1050 °C
97 Bk berkelium (beta)
use	1259 K	986 °C	1807 °F
WEL	1259 K	986 °C	1807 °F
CRC		986 °C
LNG		986 °C
98 Cf californium (Cf-252 ?)
use	1173 K	900 °C	1652 °F
WEL	1173 K	900 °C	1652 °F
CRC		900 °C
LNG		(Cf-252) 900 °C
99 Es einsteinium
use	1133 K	860 °C	1580 °F
WEL	1133 K	860 °C	1580 °F
CRC		860 °C
LNG		860 °C
100 Fm fermium (Fm-257 ?)
use	1800 K	1527 °C	2781 °F
WEL	1800 K	1527 °C	2781 °F
CRC		1527 °C
LNG		(Fm-257) 1527 °C
101 Md mendelevium
use	1100 K	827 °C	1521 °F
WEL	1100 K	827 °C	1521 °F
CRC		827 °C
102 No nobelium
use	1100 K	827 °C	1521 °F
WEL	1100 K	827 °C	1521 °F
CRC		827 °C
103 Lr lawrencium
use	1900 K	1627 °C	2961 °F
WEL	1900 K	1627 °C	2961 °F
CRC		1627 °C
LNG		1627 °C

Notes:

All values at standard pressure (101.325 kPa) unless noted. Triple point temperature values (marked "tp") are not valid at standard pressure.

References:

a) WEL-

As quoted at http://www.webelements.com/ from these sources:

A.M. James and M.P. Lord in Macmillan's Chemical and Physical Data, Macmillan, London, UK, 1992.
G.W.C. Kaye and T.H. Laby in Tables of physical and chemical constants, Longman, London, UK, 15th edition, 1993.

b) CRC-

As quoted from various sources in an online version of:

c) CR2-

Melting point data (where different to above) from an online version of:

d) LNG-

David R. Lide (ed), CRC Handbook of Chemistry and Physics, 84th Edition. CRC Press. Boca Raton, Florida, 2003; Section 4, Properties of the Elements and Inorganic Compounds; Density of Molten Elements and Representative Salts
J.A. Dean (ed), Lange's Handbook of Chemistry (15th Edition), McGraw-Hill, 1999; Section 3; Table 3.2 Physical Constants of Inorganic Compounds

Related Keywords :

Click on blue links below for related keyword searches >

Translate

Text Resize

Contact READE

Eastern Region (USA)

Western Region (USA)

Latin America & Southern Europe (PMA)

Request a Quote

READE SuperSite Search

Product Search

Services Search

Translate

Text Resize

Contact READE

Join Us On...

Follow Us On...