tag rule

Melting Points of the Elements from READE

{glossarbot=disable}Melting point

1 H hydrogen (H2)

use

14.01 K

-259.14 °C

-434.45 °F

WEL

14.01 K

-259.14 °C

-434.45 °F

CRC

 

-259.34 °C

 

LNG

 

-259.35 °C

 

2 He helium

use

0.95 K (at 2.5 MPa)

-272.2 °C (at 2.5 MPa)

-458 °F (at 2.5 MPa)

WEL

0.95 K

-272.2 °C

-458 °F

LNG

 

-272.15 °C (at 25 atm)

 

3 Li lithium

use

453.69 K

180.54 °C

356.97 °F

WEL

453.69 K

180.54 °C

356.97 °F

CRC

 

180.50 °C

 

LNG

 

180.54 °CC

 

beryllium

usese

1560 K

1287 °C

2349 °F

WEL

1560 K

1287 °C

2349 °F

CRC

 

1287 °C

 

LNG

 

1287 °C

 

5 B boron

use

2349 K

2076 °C

3769 °F

WEL

2349 K

2076 °C

3769 °F

CRC

 

2075 °C

 

LNG

 

2076 °C

 

6 C carbon (graphite)

use

 

 

 

WEL

 ? (3800 K)

 ? (3527 °C)

 ? (6381 °F)

CRC

 

tp 4489 °C (at 10.3 MPa)

 

LNG

 

subl. (3915–4020) °C

 

6 C carbon (diamond)

use

 

 

 

WEL

 ? (3800 K)

 ? (3527 °C)

 ? (6381 °F)

CRC

 

4440 °C (at 12.4 GPa)

 

LNG

 

(at 63.5 atm) 3500 °C

 

7 N nitrogen (N2)

use

63.15 K

-210.00 °C

-346.00 °F

WEL

63.05 K

-210.1 °C

-346.18 °F

CRC

 

-210.00 °C

 

LNG

 

-210.01 °C

 

8 O oxygen (O2)

use

54.36 K

-218.79 °C

-361.82 °F

WEL

54.8 K

-218.3 °C

-360.9 °F

CRC

 

-218.79 °C

 

LNG

 

-218.4 °C

 

9 F fluorine (F2)

use

53.53 K

-219.62 °C

-363.32 °F

WEL

53.53 K

-219.62 °C

-363.32 °F

CRC

 

tp -219.67 °C

 

LNG

 

-219.61 °C

 

10 Ne neon

use

24.56 K

-248.59 °C

-415.46 °F

WEL

24.56 K

-248.59 °C

-415.46 °F

CRC

 

-248.59 °C

 

LNG

 

-248.67 °C

 

11 Na sodium

use

370.87 K

97.72 °C

207.9 °F

WEL

370.87 K

97.72 °C

207.9 °F

CRC

 

97.80 °C

 

LNG

 

97.82 °C

 

12 Mg magnesium

use

923 K

650 °C

1202 °F

WEL

923 K

650 °C

1202 °F

CRC

 

650 °C

 

LNG

 

651 °C

 

13 Al aluminium

use

933.47 K

660.32 °C

1220.58 °F

WEL

933.47 K

660.32 °C

1220.58 °F

CRC

 

660.32 °C

 

LNG

 

660.323 °C

 

freezing point 933.473 K (660.323 °C) fixed point on ITS-90

14 Si silicon

use

1687 K

1414 °C

2577 °F

WEL

1687 K

1414 °C

2577 °F

CRC

 

1414 °C

 

LNG

 

1412 °C

 

15 P phosphorus (white)

use

317.30 K

44.15 °C

111.47 °F

WEL

317.3 K

44.2 °C

111.6 °F

CRC

 

44.15 °C

 

LNG

 

44.15 °C

 

15 P phosphorus (red)

use

870 K

597 °C

1107 °F

CRC

 

tp 590 °C

 

LNG

 

597 °C

 

15 P phosphorus (black)

use

883 K

610 °C

1130 °F

CRC

 

610 °C

 

LNG

 

 

 

16 S sulfur (orthorhombic, alpha)

use

(trans. to beta) 368.4 K

(trans. to beta) 95.3 °C

(trans. to beta) 203.5 °F

CRC

 

(trans. to mono) 95.3 °C

 

LNG

 

(trans. to beta) 94.5 °C

 

16 S sulfur (monoclinic, beta, trans. slowly to alpha)

use

388.36 K

115.21 °C

239.38 °F

WEL

388.36 K

115.21 °C

239.38 °F

CRC

 

119.6 °C

 

LNG

 

115.21 °C

 

16 S sulfur (gamma)

use

380.0 K

106.8 °C

224.2 °F

LNG

 

106.8 °C

 

17 Cl chlorine (Cl2)

use

171.6 K

-101.5 °C

-150.7 °F

WEL

171.6 K

-101.5 °C

-150.7 °F

CRC

 

-101.5 °C

 

LNG

 

-101.5 °C

 

18 Ar argon

use

83.80 K

-189.35 °C

-308.83 °F

WEL

83.8 K

-189.3 °C

-308.7 °F

CRC

 

-189.35 °C

 

LNG

 

-189.38 °C

 

19 K potassium

use

336.53 K

63.38 °C

146.08 °F

WEL

336.53 K

63.38 °C

146.08 °F

CRC

 

63.5 °C

 

CR2

 

63.38 °C

 

LNG

 

63.38 °C

 

20 Ca calcium

use

1115 K

842 °C

1548 °F

WEL

1115 K

842 °C

1548 °F

CRC

 

842 °C

 

LNG

 

842 °C

 

21 Sc scandium

use

1814 K

1541 °C

2806 °F

WEL

1814 K

1541 °C

2806 °F

CRC

 

1541 °C

 

LNG

 

1541 °C

 

22 Ti titanium (hexagonal)

use

1941 K

1668 °C

3034 °F

WEL

1941 K

1668 °C

3034 °F

CRC

 

1668 °C

 

LNG

 

1668 °C

 

23 V vanadium

use

2183 K

1910 °C

3470 °F

WEL

2183 K

1910 °C

3470 °F

CRC

 

1910 °C

 

LNG

 

1917 °C

 

24 Cr chromium

use

2180 K

1907 °C

3465 °F

WEL

2180 K

1907 °C

3465 °F

CRC

 

1907 °C

 

LNG

 

1907 °C

 

25 Mn manganese

use

1519 K

1246 °C

2275 °F

WEL

1519 K

1246 °C

2275 °F

CRC

 

1246 °C

 

LNG

 

(face-centered tetragonal) 1244 °C

 

26 Fe iron

use

1811 K

1538 °C

2800 °F

WEL

1811 K

1538 °C

2800 °F

CRC

 

1538 °C

 

LNG

 

1535 °C

 

27 Co cobalt

use

1768 K

1495 °C

2723 °F

WEL

1768 K

1495 °C

2723 °F

CRC

 

1495 °C

 

LNG

 

1494 °C

 

28 Ni nickel

use

1728 K

1455 °C

2651 °F

WEL

1728 K

1455 °C

2651 °F

CRC

 

1455 °C

 

LNG

 

1453 °C

 

29 Cu copper

use

1357.77 K

1084.62 °C

1984.32 °F

WEL

1357.77 K

1084.62 °C

1984.32 °F

CRC

 

1084.62 °C

 

LNG

 

1084.62 °C

 

freezing point 1357.77 K (1084.62 °C) fixed point on ITS-90

30 Zn zinc

use

692.68 K

419.53 °C

787.15 °F

WEL

692.68 K

419.53 °C

787.15 °F

CRC

 

419.53 °C

 

LNG

 

419.527 °C

 

freezing point 692.677 K (419.527 °C) fixed point on ITS-90

31 Ga gallium

use

302.9146 K

29.7646 °C

85.5763 °F

WEL

302.91 K

29.76 °C

85.57 °F

CRC

 

tp 29.771 °C

 

CR2

 

29.76 °C

 

LNG

 

29.7646 °C

 

melting point 302.9146 K (29.7646 °C) fixed point on ITS-90

32 Ge germanium

use

1211.40 K

938.25 °C

1720.85 °F

WEL

1211.4 K

938.3 °C

1720.9 °F

CRC

 

938.25 °C

 

LNG

 

937.3 °C

 

33 As arsenic

use

1090 K

817 °C

1503 °F

WEL

1090 K

817 °C

1503 °F

CRC

 

tp 817 °C (at 3.70 MPa)

 

CR2

 

817 °C

 

LNG

 

817 °C

 

34 Se selenium (hexagonal, gray)

use

494 K

221 °C

430 °F

WEL

494 K

221 °C

430 °F

CRC

 

220.5 °C

 

CR2

 

221 °C

 

LNG

 

217 °C

 

34 Se selenium (vitreous)

use

(trans. to gray) 453 K

(trans. to gray) 180 °C

(trans. to gray) 356 °F

CRC

 

(trans. to gray) 180 °C

 

35 Br bromine (Br2)

use

265.8 K

-7.3 °C

19 °F

WEL

265.8 K

-7.3 °C

19 °F

CRC

 

-7.2 °C

 

LNG

 

-7.25 °C

 

36 Kr krypton

use

115.79 K

-157.36 °C

-251.25 °F

WEL

115.79 K

-157.36 °C

-251.25 °F

CRC

 

tp -157.38 °C (at 73.2 kPa)

 

LNG

 

-157.36 °C

 

37 Rb rubidium

use

312.46 K

39.31 °C

102.76 °F

WEL

312.46 K

39.31 °C

102.76 °F

CRC

 

39.30 °C

 

CR2

 

39.31 °C

 

LNG

 

39.31 °C

 

38 Sr strontium

use

1050 K

777 °C

1431 °F

WEL

1050 K

777 °C

1431 °F

CRC

 

777 °C

 

LNG

 

757 °C

 

39 Y yttrium

use

1799 K

1526 °C

2779 °F

WEL

1799 K

1526 °C

2779 °F

CRC

 

1522 °C

 

CR2

 

1526 °C

 

LNG

 

1522 °C

 

40 Zr zirconium

use

2128 K

1855 °C

3371 °F

WEL

2128 K

1855 °C

3371 °F

CRC

 

1855 °C

 

LNG

 

1852 °C

 

41 Nb niobium

use

2750 K

2477 °C

4491 °F

WEL

2750 K

2477 °C

4491 °F

CRC

 

2477 °C

 

LNG

 

2468 °C

 

42 Mo molybdenum

use

2896 K

2623 °C

4753 °F

WEL

2896 K

2623 °C

4753 °F

CRC

 

2623 °C

 

LNG

 

2622 °C

 

43 Tc technetium (Tc-98 ?)

use

2430 K

2157 °C

3915 °F

WEL

2430 K

2157 °C

3915 °F

CRC

 

2157 °C

 

LNG

 

(Tc-98) 2157 °C

 

44 Ru ruthenium

use

2607 K

2334 °C

4233 °F

WEL

2607 K

2334 °C

4233 °F

CRC

 

2334 °C

 

LNG

 

2334 °C

 

45 Rh rhodium

use

2237 K

1964 °C

3567 °F

WEL

2237 K

1964 °C

3567 °F

CRC

 

1964 °C

 

LNG

 

1963 °C

 

46 Pd palladium

use

1828.05 K

1554.9 °C

2830.82 °F

WEL

1828.05 K

1554.9 °C

2830.82 °F

CRC

 

1554.9 °C

 

LNG

 

1555 °C

 

47 Ag silver

use

1234.93 K

961.78 °C

1763.2 °F

WEL

1234.93 K

961.78 °C

1763.2 °F

CRC

 

961.78 °C

 

LNG

 

961.78 °C

 

freezing point 1234.93 K (961.78 °C) fixed point on ITS-90

48 Cd cadmium

use

594.22 K

321.07 °C

609.93 °F

WEL

594.22 K

321.07 °C

609.93 °F

CRC

 

321.07 °C

 

LNG

 

321 °C

 

49 In indium

use

429.75 K

156.60 °C

313.88 °F

WEL

429.75 K

156.6 °C

313.88 °F

CRC

 

156.60 °C

 

LNG

 

156.60 °C

 

freezing point 429.7485 K (156.5985 °C) fixed point on ITS-90

50 Sn tin (white)

use

505.08 K

231.93 °C

449.47 °F

WEL

505.08 K

231.93 °C

449.47 °F

CRC

 

231.93 °C

 

LNG

 

231.928 °C

 

freezing point 505.078 K (231.928 °C) fixed point on ITS-90

51 Sb antimony

use

903.78 K

630.63 °C

1167.13 °F

WEL

903.78 K

630.63 °C

1167.13 °F

CRC

 

630.63 °C

 

LNG

 

630.7 °C

 

52 Te tellurium

use

722.66 K

449.51 °C

841.12 °F

WEL

722.66 K

449.51 °C

841.12 °F

CRC

 

449.51 °C

 

LNG

 

449.8 °C

 

53 I iodine (I2)

use

386.85 K

113.7 °C

236.66 °F

WEL

386.85 K

113.7 °C

236.66 °F

CRC

 

113.7 °C

 

LNG

 

113.60 °C

 

54 Xe xenon

use

161.4 K

-111.7 °C

-169.1 °F

WEL

161.4 K

-111.7 °C

-169.1 °F

CRC

 

tp -111.79 °C (at 81.6 kPa)

 

LNG

 

-111.8 °C

 

55 Cs caesium

use

301.59 K

28.44 °C

83.19 °F

WEL

301.59 K

28.44 °C

83.19 °F

CRC

 

28.5 °C

 

CR2

 

28.44 °C

 

LNG

 

28.44 °C

 

56 Ba barium

use

1000 K

727 °C

1341 °F

WEL

1000 K

727 °C

1341 °F

CRC

 

727 °C

 

LNG

 

726.9 °C

 

57 La lanthanum

use

1193 K

920 °C

1688 °F

WEL

1193 K

920 °C

1688 °F

CRC

 

918 °C

 

CR2

 

920 °C

 

LNG

 

920 °C

 

58 Ce cerium

use

1068 K

795 °C

1463 °F

WEL

1068 K

795 °C

1463 °F

CRC

 

798 °C

 

CR2

 

799 °C

 

LNG

 

795 °C

 

59 Pr praseodymium

use

1208 K

935 °C

1715 °F

WEL

1208 K

935 °C

1715 °F

CRC

 

931 °C

 

LNG

 

935 °C

 

60 Nd neodymium

use

1297 K

1024 °C

1875 °F

WEL

1297 K

1024 °C

1875 °F

CRC

 

1021 °C

 

CR2

 

1016 °C

 

LNG

 

1024 °C

 

61 Pm promethium (Pm-147 ?)

use

1315 K

1042 °C

1908 °F

WEL

1373 K

1100 °C

2012 °F

CRC

 

1042 °C

 

LNG

 

(Pm-147) 1080 °C

 

62 Sm samarium

use

1345 K

1072 °C

1962 °F

WEL

1345 K

1072 °C

1962 °F

CRC

 

1074 °C

 

CR2

 

1072 °C

 

LNG

 

1074 °C

 

63 Eu europium

use

1099 K

826 °C

1519 °F

WEL

1099 K

826 °C

1519 °F

CRC

 

822 °C

 

LNG

 

822 °C

 

64 Gd gadolinium

use

1585 K

1312 °C

2394 °F

WEL

1585 K

1312 °C

2394 °F

CRC

 

1313 °C

 

CR2

 

1314 °C

 

LNG

 

1312 °C

 

65 Tb terbium

use

1629 K

1356 °C

2473 °F

WEL

1629 K

1356 °C

2473 °F

CRC

 

1356 °C

 

CR2

 

1359 °C

 

LNG

 

1356 °C

 

66 Dy dysprosium

use

1680 K

1407 °C

2565 °F

WEL

1680 K

1407 °C

2565 °F

CRC

 

1412 °C

 

CR2

 

1411 °C

 

LNG

 

1412 °C

 

67 Ho holmium

use

1734 K

1461 °C

2662 °F

WEL

1734 K

1461 °C

2662 °F

CRC

 

1474 °C

 

CR2

 

1472 °C

 

LNG

 

1474 °C

 

68 Er erbium

use

1802 K

1529 °C

2784 °F

WEL

1770 K

1497 °C

2727 °F

CRC

 

1529 °C

 

LNG

 

1529 °C

 

talk

  • The Gmelin rare earths handbook lists 1522 °C and 1550 °C as two melting points given in the literature, the most recent reference [Handbook on the chemistry and physics of rare earths, vol.12 (1989)] is given with 1529 °C.

  • The World Book encyclopedia from 2002 lists 1529 °C.

69 Tm thulium

use

1818 K

1545 °C

2813 °F

WEL

1818 K

1545 °C

2813 °F

CRC

 

1545 °C

 

LNG

 

1545 °C

 

70 Yb ytterbium

use

1097 K

824 °C

1515 °F

WEL

1097 K

824 °C

1515 °F

CRC

 

819 °C

 

CR2

 

824 °C

 

LNG

 

819 °C

 

71 Lu lutetium

use

1925 K

1652 °C

3006 °F

WEL

1925 K

1652 °C

3006 °F

CRC

 

1663 °C

 

LNG

 

1663 °C

 

72 Hf hafnium

use

2506 K

2233 °C

4051 °F

WEL

2506 K

2233 °C

4051 °F

CRC

 

2233 °C

 

LNG

 

2227 °C

 

73 Ta tantalum

use

3290 K

3017 °C

5463 °F

WEL

3290 K

3017 °C

5463 °F

CRC

 

3017 °C

 

LNG

 

2996 °C

 

74 W tungsten

use

3695 K

3422 °C

6192 °F

WEL

3695 K

3422 °C

6192 °F

CRC

 

3422 °C

 

LNG

 

3387 °C

 

75 Re rhenium

use

3459 K

3186 °C

5767 °F

WEL

3459 K

3186 °C

5767 °F

CRC

 

3186 °C

 

LNG

 

3180 °C

 

76 Os osmium

use

3306 K

3033 °C

5491 °F

WEL

3306 K

3033 °C

5491 °F

CRC

 

3033 °C

 

LNG

 

3045 °C

 

77 Ir iridium

use

2719 K

2446 °C

4435 °F

WEL

2739 K

2466 °C

4471 °F

CRC

 

2446 °C

 

LNG

 

2447 °C

 

78 Pt platinum

use

2041.4 K

1768.3 °C

3214.9 °F

WEL

2041.4 K

1768.3 °C

3214.9 °F

CRC

 

1768.4 °C

 

LNG

 

1769 °C

 

79 Au gold

use

1337.33 K

1064.18 °C

1947.52 °F

WEL

1337.33 K

1064.18 °C

1947.52 °F

CRC

 

1064.18 °C

 

LNG

 

1064.18 °C

 

freezing point 1337.33 K (1064.18 °C) fixed point on ITS-90

80 Hg mercury

use

234.32 K

-38.83 °C

-37.89 °F

WEL

234.32 K

-38.83 °C

-37.89 °F

CRC

 

tp -38.837 °C

 

LNG

 

-38.83 °C

 

81 Tl thallium

use

577 K

304 °C

579 °F

WEL

577 K

304 °C

579 °F

CRC

 

304 °C

 

LNG

 

303.5 °C

 

82 Pb lead

use

600.61 K

327.46 °C

621.43 °F

WEL

600.61 K

327.46 °C

621.43 °F

CRC

 

327.46 °C

 

LNG

 

327.43 °C

 

83 Bi bismuth

use

544.7 K

271.5 °C

520.7 °F

WEL

544.4 K

271.3 °C

520.3 °F

CRC

 

271.40 °C

 

LNG

 

271.5 °C

 

84 Po polonium

use

527 K

254 °C

489 °F

WEL

527 K

254 °C

489 °F

CRC

 

254 °C

 

LNG

 

254 °C

 

85 At astatine

use

575 K

302 °C

576 °F

WEL

575 K

302 °C

576 °F

CRC

 

302 °C

 

LNG

 

302 °C

 

86 Rn radon

use

202 K

-71 °C

-96 °F

WEL

202 K

-71 °C

-96 °F

CRC

 

-71 °C

 

LNG

 

-71 °C

 

87 Fr francium

use

300 K

27 °C

80 °F

CRC

 

27 °C

 

88 Ra radium

use

973 K

700 °C

1292 °F

WEL

973 K

700 °C

1292 °F

CRC

 

700 °C

 

LNG

 

700.1 °C

 

89 Ac actinium (Ac-227 ?)

use

circa 1323 K

circa 1050 °C

circa 1922 °F

WEL

1323 K

1050 °C

1922 °F

CRC

 

1051 °C

 

LNG

 

(Ac-227) 1050(50) °C

 

90 Th thorium

use

2115 K

1842 °C

3348 °F

WEL

2115 K

1842 °C

3348 °F

CRC

 

1750 °C

 

LNG

 

1750 °C

 

91 Pa protactinium

use

1841 K

1568 °C

2854 °F

WEL

1841 K

1568 °C

2854 °F

CRC

 

1572 °C

 

92 U uranium

use

1405.3 K

1132.2 °C

2070 °F

WEL

1405.3 K

1132.2 °C

2070 °F

CRC

 

1135 °C

 

LNG

 

1135 °C

 

93 Np neptunium

use

917 K

644 °C

1191 °F

WEL

910 K

637 °C

1179 °F

CRC

 

644 °C

 

LNG

 

644 °C

 

94 Pu plutonium

use

912.5 K

639.4 °C

1182.9 °F

WEL

912.5 K

639.4 °C

1182.9 °F

CRC

 

640 °C

 

LNG

 

639.5 °C

 

95 Am americium

use

1449 K

1176 °C

2149 °F

WEL

1449 K

1176 °C

2149 °F

CRC

 

1176 °C

 

LNG

 

1176 °C

 

96 Cm curium (Cm-244 ?)

use

1613 K

1340 °C

2444 °F

WEL

1613 K

1340 °C

2444 °F

CRC

 

1345 °C

 

LNG

 

(Cm-244) 1340 °C

 

97 Bk berkelium (alpha)

use

1323 K

1050 °C

1922 °F

CRC

 

1050 °C

 

LNG

 

1050 °C

 

97 Bk berkelium (beta)

use

1259 K

986 °C

1807 °F

WEL

1259 K

986 °C

1807 °F

CRC

 

986 °C

 

LNG

 

986 °C

 

98 Cf californium (Cf-252 ?)

use

1173 K

900 °C

1652 °F

WEL

1173 K

900 °C

1652 °F

CRC

 

900 °C

 

LNG

 

(Cf-252) 900 °C

 

99 Es einsteinium

use

1133 K

860 °C

1580 °F

WEL

1133 K

860 °C

1580 °F

CRC

 

860 °C

 

LNG

 

860 °C

 

100 Fm fermium (Fm-257 ?)

use

1800 K

1527 °C

2781 °F

WEL

1800 K

1527 °C

2781 °F

CRC

 

1527 °C

 

LNG

 

(Fm-257) 1527 °C

 

101 Md mendelevium

use

1100 K

827 °C

1521 °F

WEL

1100 K

827 °C

1521 °F

CRC

 

827 °C

 

102 No nobelium

use

1100 K

827 °C

1521 °F

WEL

1100 K

827 °C

1521 °F

CRC

 

827 °C

 

103 Lr lawrencium

use

1900 K

1627 °C

2961 °F

WEL

1900 K

1627 °C

2961 °F

CRC

 

1627 °C

 

LNG

 

1627 °C

 

Notes:

  • All values at standard pressure (101.325 kPa) unless noted. Triple point temperature values (marked "tp") are not valid at standard pressure.

References:

a) WEL-

As quoted at http://www.webelements.com/ from these sources:

  • A.M. James and M.P. Lord in Macmillan's Chemical and Physical Data, Macmillan, London, UK, 1992.

  • G.W.C. Kaye and T.H. Laby in Tables of physical and chemical constants, Longman, London, UK, 15th edition, 1993.

b) CRC-

As quoted from various sources in an online version of:

c) CR2-

Melting point data (where different to above) from an online version of:

 

d) LNG-

  • David R. Lide (ed), CRC Handbook of Chemistry and Physics, 84th Edition. CRC Press. Boca Raton, Florida, 2003; Section 4, Properties of the Elements and Inorganic Compounds; Density of Molten Elements and Representative Salts

  • J.A. Dean (ed), Lange's Handbook of Chemistry (15th Edition), McGraw-Hill, 1999; Section 3; Table 3.2 Physical Constants of Inorganic Compounds